INOZINC
السعر عند الطلب
كلّ منتجات المتجر ←
الوصف
INOZINC is a two-component water base inorganic zinc silicate primer
المواصفات
| اللمسة النهائية | flat |
| العبوة | Component A (liquid) : 3 Kg in 1 metal can Component B (powder) : 7 Kg in 1 metal can |
| اللون | grey |
| Application Instruction — Mixing Ratio | 3Kg (Comp A) to 7Kg (Comp B) |
| Application Instruction — Mixing | Add Comp.B (powder) to Comp. A (liquid) and stir well before application in order to ensure that a uniform consistency is achieved. Never mix more material than can be used within potlife. Mixed materials not used within potlife must be discarded |
| Application Instruction — Pot life | 8 hours (higher temperatures will shorten polife sharply) |
| Application Instruction — Thinner / Cleaner | Do not thin. Clean applying tools by hot water |
| Technical Information — Volume Solids | 65 % |
| Technical Information — Flexibility | Very Good |
| Technical Information — Recommended film thickness | 75-125 microns “dry” |
| التغطية (م²/لتر) | 8.7 m²/L at 75 microns “dry” |
| Technical Information — Water resistance | Excellent |
| Technical Information — Abrasian Resistance | Excellent |
| عدد الطبقات | 1 |
| Technical Information — Specific Gravity (mixed) | 2.79 kg/L (DIN 51757) |
| زمن الجفاف | 30 minutes (ASTM-D1640) |
| Drying Time — Fully Cured | 2 hours |
| Drying Time — Note | Drying times can be affected by many factors such as temperature, ventilation and coat thickness. Relative humidity should not exceed 85%. Higher temperatures will shorten the drying times |
| Technical Information — Temperature Resistance | 375 ?C |
| Application Instruction — Application Temperature | 5-40 ?C at a RH not more than 85% |
| Technical Information — VOC | 0.0 g/L |
| Application Instruction — Curing | The reaction between the two-component (A & B) can not be guaranteed unless a temperature of at least 5°C is maintained for the mixture and the substrate until complete curing. Temperature of substrate should be at least 3°C above dew point to avoid moisture condensation during application. Relative |
| Technical Information — Weather Resistance | Excellent |
| Technical Information — Solvent Splash and Spill Resistance | Excellent |
| Technical Information — Component B | powder |