EPX12 ALU
السعر عند الطلب
كلّ منتجات المتجر ←
الوصف
A two-component (A & B) aluminium epoxy primer/coat
المواصفات
| اللمسة النهائية | Matt (ASTM D-523) |
| العبوة | Component A “base” : 3.6 L in metal can Component B “drier: CAT10 “ : 0.9 L in metal can |
| Application Instruction — Mixing Ratio | by volume) 4 to 1 (A to B) |
| Application Instruction — Mixing | The individual components should be thoroughly stirred before the two are mixed together. Combine components (A & B) in supplied proportions and mix thoroughly using a slow speed mixer for at least 3 minutes to achieve uniform consistency; “DO NOT USE HIGH SPEED MIXER”. Never mix more material than |
| Application Instruction — Pot life | 20°C) 24 hours (higher temperatures will shorten the potlife sharply) |
| Application Instruction — Thinner / Cleaner | S405 “Known as Epoxsol” is uesd for thinning or cleaning. Mixing ratio with thinner depends mainly on temperature and on method of application. For example: At 20°C airless spray application will need no dilution. Other methods of application will need approx 15% by volume thinner S405. The higher t |
| Technical Information — Volume Solids | 45.1% (ASTM-D2687) |
| Technical Information — Flexibility | Good |
| Technical Information — Recommended film thickness | 75 microns “dry” |
| التغطية (م²/لتر) | 6 m²/L at 100 microns "dry" |
| Technical Information — Water resistance | Excellent |
| Technical Information — Abrasian Resistance | Fair |
| Technical Information — Chemical Resistance | Good |
| Technical Information — Solvent Resistance | Good |
| عدد الطبقات | 1-2 |
| Technical Information — Specific Gravity (mixed) | 1.07 kg/L (ASTM-D1475) |
| زمن الجفاف | 10 hours “minimum recoat time”. 24 hours “maximum recoat time" (ASTM -D1640) |
| Drying Time — Fully Cured | 7 days |
| Drying Time — Note | Drying times can be affected by many factors such as temperature, ventilation and coat thickness. Higher temperatures will shorten the drying times |
| Technical Information — Weather Resistance | Excellent |