EPX105 GF
السعر عند الطلب
كلّ منتجات المتجر ←
الوصف
EPX105 GF is a two-component (A & B) high solids glass flake epoxy
المواصفات
| اللمسة النهائية | Flat (ASTM-D523) |
| العبوة | Component A “base” 3.7 L in US Gallon Component B “drier” 3.15 L in US Gallon |
| اللون | Against order for CAT32, dark colors for CAT22 |
| Application Instruction — Mixing Ratio | (by volume) 3.7 to 3.15 (A to B) |
| Application Instruction — Mixing | The individual components of EPX105 GF should be thoroughly stirred before the two are mixed together. Combine components (A & B) in supplied proportions and mix thoroughly using a slow speed mixer for at least 3 minutes to achieve uniform consistency; “DO NOT USE HIGH SPEED MIXER”. Never mix more m |
| Application Instruction — Pot life | 45 minutes, higher temperatures will shorten the potlife sharply) |
| Application Instruction — Thinner / Cleaner | S405 “known as Epoxsol” is used for thinning and cleaning. Due to potlife limitations, clean clean all mixing equipment and application tools by thinner immediately after application is completed |
| Technical Information — Volume Solids | 91.9 % (ASTM-D2697) |
| Technical Information — Flexibility | Excellent |
| Technical Information — Recommended film thickness | 250-1000 microns “dry”, thickness of 1000 microns should be applied in very corrosive environments |
| التغطية (م²/لتر) | 3.7 m²/L at 250 microns “dry” |
| Technical Information — Water resistance | Excellent |
| Technical Information — Abrasian Resistance | Excellent |
| Technical Information — Chemical Resistance | Excellent (CAT22), Very good (CAT32) "a separate leaflet CHR01 is available" |
| Technical Information — Solvent Resistance | Very good (CAT22), good (CAT32) "a separate leaflet CHR01 is available" |
| عدد الطبقات | 1-2 |
| Technical Information — Specific Gravity (mixed) | 1.508 kg/L (ASTM-D1475) |
| زمن الجفاف | 24 hours “minimum recoat time”. 2 days “maximum recoat time” (ASTM-D1640) |
| Drying Time — Fully Cured | 7 days |
| Drying Time — Note | Drying times can be affected by many factors such as temperature, ventilation and coat thickness. Higher temperatures will shorten the drying times |